Atmosphere effect on sintering behaviour of astaloy CrM and astaloy CrL Höganäs powders with manganese and carbon additions

Dilatometric data for Astaloy CrM (3% Cr-0.5% Mo) and Astaloy CrL (1.5% Cr-0.2% Mo) powders with additions of 0.3% carbon and 3.0% manganese during sintering cycles up to 1120 and 1250 ° C in different atmospheres are reported. For comparison, also Astaloy CrM and Astaloy CrL powders were investigated. Starting with green densities of approx. 6.8 g/cm3, the final density of sintered compacts was influenced mainly by the sintering temperature, while the results showed the only minor effect of the sintering atmosphere on the final dimensional changes. However, the sintering atmosphere influences the sintering behaviour, microstructure and the final chemical composition of sintered compacts. In sintered and in the dilatometer cooled Mn-Cr-Mo-C steels predominantly bainitic structures were obtained.

---

Praca przedstawia wyniki badań dylatometrycznych procesu spiekania mieszanek proszków zawierających, jako podstawowe, proszki Astaloy CrM (3% Cr-0.5% Mo) i Astaloy CrL (1.5% Cr-0.2% Mo) oraz dodatki 3% mas. Mn i 0.3% mas. C. Spiekanie izotermiczne realizowane było w dwóch temperaturach: 1120 ° C i 1250 ° C, a atmosferami spiekania były gazy: azot, mieszanina 95% obj. azotu + 5% obj. wodoru i argon. Gęstość spieków determinowana jest głównie temperatura spiekania, a wpływ atmosfery jest nieznaczny. Jednakże od rodzaju atmosfery spiekania uzależnione jest zachowanie się materiałów w trakcie cykli termicznych, jakim są poddane podczas spiekania. Atmosfera spiekania ma również wpływ na mikrostrukturę spieków oraz na zmiany składu chemicznego towarzyszące spiekaniu. Głównym składnikiem struktury spieków uzyskanej bezpośrednio po spiekaniu w warunkach chłodzenia dostępnych w dylatometrze był bainit.