Comparative Characteristics of the AlZr Alloy Materials Electrical and Mechanical Properties

The subject of the present article consists in obtaining the wire production material with the controlled, during the heat treatment, level of electrical and mechanical properties. In the case of the AlZr alloys the appropriate strength properties are obtained in the technological process through the introduction of the specified value of the cold working (work-hardening). In turn,the AlZr alloy resistivity value is dependent on both the amount of the zircon additive and its placement characteristics in the aluminium structure (solid solution or emissions). The paper presents comparative resistivity and hardness tests of the AlZr alloy material with the zircon content ranging from 0.05 to 0.32% mas. Zr produced in the continuous casting technology as well as in the continuous casting and rolling technology.

---

Problematyka tematu artykułu, polega na uzyskaniu materiału do produkcji drutów o kontrolowanym, w procesie obróbki cieplnej poziomie własności elektrycznych i mechanicznych. W przypadku stopów AlZr uzyskanie odpowiednich własności wytrzymałościowych jest osiągane w procesie technologicznym poprzez wprowadzenie określonej wartości odkształcenia na zimno (umocnienie odkształceniowe). Z kolei wartość rezystywności stopu AlZr jest uzależniona zarówno od ilości dodatku cyrkonu jak i charakteru jego ulokowania w strukturze aluminium (roztwór stały lub wydzielenia). W pracy przedstawiono badania porównawcze rezystywności i twardości, materiału ze stopów AlZr, o zawartości cyrkonu w zakresie od 0,05 do 0,32% mas. Zr. wytworzonego w technologii ciągłego odlewania oraz w technologii ciągłego odlewania i walcowania.