The effect of deformation route in Equal Channel Angular Pressing on mechanical properties of aluminum alloy 1050

Annealed samples of commercial purity aluminium (1050) were processed by Equal Channel Angular Pressing (ECAP) at room temperature for up to eight passes. ECAP was conducted by using three processing routes (schemes). Tensile tests and micro hardness were conducted to evaluate variation of mechanical properties after each pass. Analysis of fractography was carried out due to investigate a fracture of the samples. The results showed that all the schemes had similar micro hardness values – around 50 HV. The tensile test results showed that the highest yield strength was achieved in the second scheme after eight passes – 186 MPa – while elongation maintained at the level of 17.4%. The value of yield strength achieved increased more than six times in proportion to annealed condition.

---

Wyżarzone próbki, wykonane ze stopu aluminium AA 1050, poddano procesowi przeciskania przez kanał kątowy (Equal Channel Angular Pressing – ECAP) w temperaturze pokojowej. Próbki przeciskano w ośmiu cyklach według trzech dróg odkształcania. W celu oceny zmian właściwości mechanicznych przeprowadzono statyczną próbę rozciągania oraz pomiar mikrotwardości. Wykonano również analizę fraktograficzną w celu obserwacji przełomów próbek. Otrzymane wyniki mikrotwardości we wszystkich schematach wykazywały zbliżone wartości – na poziomie 50 HV. Statyczna próba rozciągania wykazała, że najwyższa granica plastyczności Rp0,2 została osiągnięta dla próbki przeciskanej według II drogi odkształcenia po ósmym cyklu i wyniosła 186 MPa przy wydłużeniu równym 17,4%. Uzyskana wartość granicy plastyczności wykazuje ponad sześciokrotny wzrost w stosunku do stanu wyżarzonego.