Influence of diffusion boriding and laser boriding on corrosion resistance Hardox 450 steel

The article presented an influence of diffusion boriding and laser boriding on microstructure, microhardness and corrosion resistance of Hardox 450 steel. After the boron modification process of Hardox 450 steel was obtained an increase result of microhardness and resistance to corrosion. After the diffusion boriding obtained needle-like microstructure of microhardness 1800-1500 HV0.1. Whereas after laser boriding microstructure was consisted of a remelted zone (MZ), heataffected zone (HAZ) and core. In the remelted zone enriched in boron the microhardness was about 1600 HV 0.1. Corrosion resistance tests showed, that the higher corrosion resistance in solutions of pH = 3.5 and pH = 7.0 have a diffusion boriding layers, whereas in the pH = 11.0, the laser boriding layers.

---

W artykule przedstawiono wpływ borowania dyfuzyjnego i laserowego na mikrostrukturę, mikrotwardość i odporność korozyjną stali Hardox 450. Po procesie modyfikacji stali Hardox 450 borem uzyskano zwiększenie mikrotwardości i odporności na korozyjnej. W wyniku procesu borowania dyfuzyjnego warstwa miała iglastą strukturę o mikrotwardości ok. 1800-1500 HV0,1. Natomiast w wyniku borowania laserowego uzyskano budowę strefową składającą się ze strefy przetopionej, strefy wpływu ciepła oraz rdzenia. W strefie przetopionej wzbogaconej w bor mikrotwardość wynosiła ok. 1600 HV0,1. Badania odporności korozyjnej wykazały, że lepszą odporność korozyjną w roztworach pH = 3,5 oraz pH = 7,0 posiadają warstwy borowane dyfuzyjnie, natomiast w pH = 11,0 warstwy borowane laserowo.