Mechanical properties of alkali-acivated binders based on copper slag

The paper describes the possibility of using copper slag, an industrial waste from smelting of copper as a basic component of hydraulic binders obtained by means of the alkaline activation. For the purpose, the aqueous sodium silicate and technical sodium metasilicate were used. Mortars, having undergone the activation process were cured under laboratory conditions (temp. 20±1°C and relative humidity approx. 60%) and were subjected to low pressure heat treatment at a temperature of 80°C. Research over the alkaline activation of slag proved that the desirable quality of alkali-activated binders is achievable just in case of using granulated copper slag, where 98% of the base mass constitutes of glassy phase, and water glass with the lowest value of silicate modulus (Mk = 1.75).

---

W artykule przedstawiono możliwości wykorzystania odpadowego żużla pomiedziowego pochodzącego z hutnictwa miedzi jako podstawowego składnika spoiw hydraulicznych otrzymanych na drodze aktywacji alkalicznej. W procesie stosowano szkło wodne sodowe o zmiennym module krzemianowym oraz techniczny metakrzemian sodu. Zaprawy po procesie aktywacji dojrzewały w warunkach laboratoryjnych (temp. 20±1°C i wilgotność względna ok. 60%) oraz były poddane niskociśnieniowej obróbce cieplnej w temperaturze 80°C. Badania nad aktywacją alkaliczną żużla dowiodły, że możliwe jest uzyskanie pożądanej jakości spoiw aktywowanych alkalicznie tylko w przypadku stosowania granulowanego żużla pomiedziowego, w którym 98% masy zasadniczej stanowi faza szklista oraz przy użyciu szkła wodnego o najniższym module krzemianowym (Mk = 1.75).