Direction of the rolling of plates made of steel grade 0H18N9 versus welding distortions
The article presents the results of tests concerning the effect of the direction of the rolling of plates made in steel 0H18N9 on welding distortions. The research-related analysis was concerned with the rolling direction in relation to the longer edge of specimens. The specimens were welded using the MAG method involving the use of pulsed arc. The acquisition of surface flatness-related data was performed using a GOM ATOS 5M blue light scanner. The analysis of the results revealed that the mean surface flatness of the specimens was similar in relation to all of the rolling directions related to analysis. However, the direction of distortions parallel and perpendicular to the weld varied depending on the direction of rolling.
Przedstawiono badanie wpływu kierunku walcowania blachy gatunku 0H18N9 na odkształcenia spawalnicze. Analizie poddano orientacje kierunku walcowania względem dłuższego brzegu próbki. Próbki spawano metodą MAG łukiem pulsującym. Akwizycji danych płaskości powierzchni dokonano za pomocą skanera światła niebieskiego GOM ATOS 5M. Na podstawie przeprowadzonej analizy stwierdzono, że średnia płaskość powierzchni próbek dla wszystkich analizowanych kierunków walcowania była zbliżona, natomiast kierunek odkształceń w kierunku równoległym i prostopadłym do spoiny różnił się w zależności od kierunku walcowania.
1. Wersja polska artykułu w wydaniu papierowym s. 47-51.
2. Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2021).