Characterization of polyurethane networks based on rapeseed oil derived polyol

Bio-based rapeseed oil (RO) polyol was synthesized by transesterification with triethanolamine. Synthesized RO/triethanolamine ester was modified with triethylene glycol (TEG) to obtain a polyol system with higher hydroxyl value, as well as with e-caprolactone (CL) to increase the carbon chain length and decrease the hydroxyl value. From these polyols there were synthesized polyurethane (PU) networks which showed good mechanical properties. It was established that with increasing urethane groups concentration and increasing crosslinking, polyurethane networks showed higher modulus of elasticity (E) and tensile strength (s). Polyurethane networks also showed higher elongation at break (e) with decreasing urethane groups concentration and decreasing crosslinking.

---

Poliol z oleju rzepakowego (RO) otrzymano metodą transestryfikacji trietanoloaminą. Otrzymany ester RO/trietanoloamina modyfikowano glikolem trietylenowym (TEG), w celu uzyskania układu poliolowego o większej zawartości grup OH, lub e-kaprolaktonem (CL) w celu zwiększenia długości łańcucha węglowego i zmniejszenia zawartości grup OH. Z otrzymanych polioli syntezowano sieci poliuretanowe (PU), które charakteryzowały się dobrymi właściwościami mechanicznymi. Stwierdzono, że wraz ze wzrostem stężenia grup uretanowych i zwiększeniem usieciowania, sieci PU charakteryzują się większym modułem sprężystości (E) i większą wytrzymałością na rozciąganie (s). Wykazano również, że zmniejszenie usieciowania i zawartości grup uretanowych w sieciach poliuretanowych wpływa na zwiększenie wydłużenia przy zerwaniu (e).