A critical review of corrosion rate calculations of Mg-Al-Li alloys using traditional mass loss measurements
The corrosion rate (CR) calculations were performed for AZ31, AZ31-4Li, AZ31-7.5Li and AZ31-15Li Mg alloys after extrusion, and after extrusion with subsequent heat treatment. CR was obtained using three different mass loss (ML) measurements: i) traditional ML measurements where weighing before and after immersion was being implied, ii) by atomic absorption spectroscopy, where number of Mg2+ ions were calculated from the solution after immersion, and iii) by ML measurements in an artificial atmosphere. As results show, there are many differences in CR results obtained by these techniques. When CR is being calculated for multi-alloying materials, all possible anodic reactions which can take place during dissolution of immersed samples in the solution, should be considered.
W pracy porównano szybkość korozji mierzoną trzema różnymi metodami dla stopów Mg-Li-Al. Szybkość korozji została obliczona w oparciu o i) grawimetryczne pomiary ubytku masy po zanurzeniu w roztworze, ii) analizę stężenia jonów Mg2+ w roztworze po zanurzenie próbek, iii) na podstawie pomiarów ubytku masy po ekspozycji próbek w komorze solnej. Na podstawie wykonanych pomiarów wskazano wady i zalety metod służących do oceny szybkości korozji stopów magnezu zawierających różne dodatki stopowe, w tym Al i Li. Wykazano, że dobór metody służącej do oceny szybkości korozji wieloskładnikowych stopów magnezu jest ściśle uzależniony od rodzaju i ilości reakcji anodowych zachodzących w trakcie ekspozycji materiału w środowisku korozyjnym.
Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).