Influence of electrolyte on capacity and corrosion resistance of anode material used in Ni-MH cells
The electrochemical capacity and corrosion resistance of the La2Ni9CoSn0.2 alloy in two different electrolytes (KOH and LiOH) at the same concentration (6 mol·dm-3) has been investigated. Higher values of capacities for the electrode during activation have been obtained in KOH solution. The corrosion current density and corrosion potential of La2Ni9CoSn0.2 alloy indicate that the electrode worked in KOH solution has a better anti-corrosion ability. The decrease of the electrochemical capacity of the alloy observed in LiOH solution can result from accelerated corrosion of the electrode material in this environment.
Badano pojemność elektrochemiczną i odporność korozyjną stopu La2Ni9CoSn0.2 w dwóch różnych roztworach elektrolitów (KOH i LiOH) o tym samym stężeniu (6 mol·dm-3). Wyższe wartości pojemności uzyskano podczas aktywacji elektrody w roztworze KOH. Gęstość prądu korozyjnego i potencjał korozyjny stopu La2Ni9CoSn0.2 wskazują na jego lepszą odporność korozyjną w roztworze KOH. Spadek pojemności elektrochemicznej stopu w roztworze LiOH może wynikać z przyspieszonej korozji materiału elektrody w tym środowisku.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.