Detonation-Sprayed WC-12%Co and WC-17%Co Diamond-Impregnated Segments

This paper presents results of investigations of WC-12%Co and WC-17%Co coatings detonation sprayed on a sintered cobalt substrate. The main objective of the present work was to establish a new production route of sandwich type diamond-impregnated segments for circular sawing of stone and other construction materials. Unalloyed cobalt was chosen as the substrate material. Prior to coating the specimens were made by means of hot pressing of Extrafine cobalt powder in a graphite mould. The segments were then coated with WC-Co. The effects of the coating process on the thickness, microhardness, microstructure and wear resistance of the deposits were investigated. The properties of the coatings were established by performing the following tests: a microstructure analysis, a point analysis of chemical composition and a linear analysis, a phase composition, a microhardness tests and abrasion resistance.

---

W pracy przedstawiono wyniki badań detonacyjnego nanoszenia powłok WC-12%Co WC-17%Co na spieki kobaltu. Badania prowadzono w celu opracowania nowej technologii wytwarzania trójwarstwowych segmentów metaliczno-diamentowych typu sandwich przeznaczonych do produkcji tarczowych pił diamentowych i innych materiałów budowlanych. Próbki do badań otrzymano z proszków kobaltu gatunku Extrafine technika prasowania na gorąco w grafitowej matrycy, a następnie na ich powierzchnie natryskano powłoki WC-Co. Badano wpływ parametrów procesu natryskiwania na grubość, mikrotwardość, mikrostrukturę i odporność na zużycie ścierne uzyskanych powłok. Przeprowadzono następujące badania uzyskanych powłok: obserwacje mikrostruktury, analizę punktową i liniową składu chemicznego; analizę składu fazowego, pomiar mikrotwardości oraz badanie odporności powłok na zużycie ścierne.