The influence of aging process parameters on selected mechanical properties of profiles from EN AW-6106 aluminium alloy
The aim of this article was to analyze the influence of temperature and time period of artificially aging process on selected mechanical properties: Brinell hardness, yield strength, tensile strength, and elongation of hot extruded profiles from EN AW-6106 aluminum alloy. The result of the conducted research has pointed out that the temperature and the time of aging process had a significant effect on the selected mechanical properties. In the study it was found that the highest mechanical properties such as the yield strength and tensile strength for analyzed aluminum alloy were achieved for samples aged in temperature of 165°C for time period of 6 hours. The value of mechanical properties required be the standards for T6 temper were achieved after 2 hours of artificial aging in temperature of 165°C.
Celem pracy była analiza wpływu temperatury i czasu procesu sztucznego starzenia na wybrane właściwości mechaniczne: twardość Brinella, umowną granice plastyczności, wytrzymałość na rozciąganie i wydłużenie wyciskanych na gorąco profili ze stopu aluminium EN AW-6106. Wyniki przeprowadzanych badań wykazały, że temperatura i czas procesu sztucznego starzenia ma istotny wpływ na wybrane do badań właściwości mechaniczne. W badaniach stwierdzono, że najwyższą wartość własności mechanicznych takich jak: umownej granicy plastyczności oraz wytrzymałości na rozciąganie uzyskano po przeprowadzonym procesie sztucznego starzenia w temperaturze 165°C przez czas 6h. Niezbędny poziom własności mechanicznych wymaganych przez normy dla stanu T6 osiągnięto już po dwóch godzinach procesu starzenia w temperaturze 165°C.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).