Analysis of technological characteristics of high-melting metal arc spraying 3Cr13

The experimental study has been done for high-melting metal arc spraying 3Cr13 technological parameters to research the influence of spraying current, spraying voltage and wire feed voltage on spraying arc and the influence of spraying current on coating temperature. Theoretically, it has been analyzed the distribution rules of spray gun jet speed field and temperature field and their influence factors. The results showed that the arc current increases along with arc voltage increase. The lower the spraying voltage is, the smaller the molten grain size becomes. However, if the arc voltage is lower than the minimum critical arc voltage of the material, the arc could not keep smooth burning. The spraying current has correspondence relationship with wire feed speed. The spraying current could be adjusted through wire feed speed adjustment. The temperature on the coating surface increases along with spraying current increase and the air velocity has almost no influence on grain’s temperature.

---

Przeprowadzono eksperymentalne badania technologicznych parametrów metalizacji łukowej natryskowej metalem o wysokiej temperaturze topnienia, typ 3Cr13. Badano wpływ prądu i napięcia metalizacji oraz przesuwu drutu na łuk metalizacji a także wpływ prądu na temperaturę powłoki. Teoretycznie zbadano wpływ tych parametrów na rozkład szybkości i temperatury w strumieniu pistoletu natryskowego. Prąd metalizacji wzrasta z napięciem. Zmniejszenie napięcia wywołuje zmniejszenie rozmiaru ziarna stopionego metalu. Jednak, zmniejszenie napięcia poniżej minimalnego dla danego materiału może spowodować, że łuk nie będzie gładki. Prąd metalizacji zależy od szybkości przesuwu drutu i musi być do niej dostosowany, Temperatura powierzchni powłoki wzrasta wraz z prądem metalizacji a szybkość strumienia powietrza nie ma wpływu na temperaturę ziarna.