Influence of time on modification effect of silumin AlSi11 with strontium and boron

Studies on the effect of time on the modification of AlSi11 silumin with variable strontium micro additives in the form of an AlSr10 master alloy and boron in an AlB4 master alloy were investigated. The results showed that the strontium micro additive resulted in a satisfactory improvement in the α(Al) + β(Si) eutectic and an increase in tensile strength (Rm) and unit elongation (A5); this is also the case two hours after adding the modifier. The simultaneous modification of silumin with AlB4 and AlSr10 causes a strong fragmentation of the alloy grains and significant improvement in Rm and A5 (also two hours after adding the modifiers).

---

Przeprowadzono badania nad wpływem czasu na modyfikację siluminu AlSi11 zmiennymi mikrododatkami strontu w postaci zaprawy AlSr10 oraz boru w postaci zaprawy AlB4. Wyniki badań wykazały, że mikrododatek strontu powoduje zadowalające uszlachetnienie eutektyki α(Al) + β(Si) i wzrost wytrzymałości na rozciąganie (Rm) oraz wydłużenia względnego (A5), także po upływie dwóch godzin po dodaniu modyfikatora. Równoczesna modyfikacja siluminu zaprawami AlB4 i AlSr10 powoduje silne rozdrobnienie ziarn stopu i istotną poprawę Rm oraz A5, również po upływie dwóch godzin po dodaniu modyfikatorów.

---

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).