FE and physical modelling of plastic deformation the two-layer Mg/Al materials
The paper has presented the results of theoretical studies and experimental tests of the plastic deformation of two- layered Mg/Al specimens. Theoretical studies were carried out using the Forge2011® computer program. Physical modeling, on the other hand, was performed using the Gleeble3800 simulator. Cuboidal specimens with dimensions of 10x15x20 mm and a cladding layer thickness of 1.5 mm were cut off from the sheets obtained in the explosive welding method. The theoretical studies and experimental tests were carried out for the temperature range from 350 to 400°C and for different strain rates. Based on the obtained investigation results it has been found that the main parameters influencing the formability of two-layered Mg/Al materials are temperature and the strain rate.
W pracy przedstawiono wyniki badań teoretycznych i do-świadczalnych plastycznego odkształcenia dwuwarstwowego materiału Mg/Al. Badania teoretyczne przeprowadzono za pomocą programu komputerowego Forge20ll®, natomiast modelowanie fizyczne wykonano za pomocą symulatora Gleeble3800. Badaniom poddano próbki prostopadłościenne o wymiarach 10x15x20 mm i grubość warstwy platerującej 1,5 mm. Dwuwarstwowy materiał, z którego pobrano próbki otrzymano metodą zgrzewania wybuchowego. Badania teoretyczne i doświadczalne wykonano dla zakresu temperatur od 300 do 400°C oraz dla różnych prędkości odkształcenia. Na podstawie otrzymanych wyników badań stwierdzono, że głównymi parametrami wpływającymi na odkształcalność prętów bimetalowych Mg/Al są temperatura oraz prędkość odkształcenia.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).