Dependence of mechanical and tribotechnical properties of multilayered TiN/ZrN coatings on deposition

C-PVD method (vacuum arc deposition of a cathodes) was used for deposition of multilayered coatings, based on TiN/ZrN systems, with different thickness of bilayers. Total thickness of the coatings was 11 – 19 μm, thickness of bilayers varied from 39 to 305 nm for different samples depending on deposition conditions. Microstructure of the coatings, mechanical and tribotechnical properties, and wear resistance were explored. Influence of the bilayer thickness on such properties of the coatings, as hardness, elasticity modulus, wear resistance and wear ratio were explored.

---

Metoda C-PVD (napylanie próżniowo-łukowe katod) została użyta do osadzania wielowarstwowych powłok, na bazie układów TiN/ZrN o zmiennej grubości pojedynczych warstw. Całkowita grubość powłoki wynosiła 11 – 19 μm, przy czym grubość pojedynczych warstw wahała się od 39 do 305 nm dla różnych próbek zależnie od warunków osadzania. Zbadano mikrostrukturę powłok, właściwości mechaniczne i trybologiczne oraz odporność na zużycie.