Electrochemical characterization of C45 carbon black-H3PMo12O40-polyvinylidene fluoride system
The paper presents research of the C45 carbon black-phosphomolybdic acid-polyvinylidene fluoride (C45-MPA-PVDF) nanocomposite in 6M KOH with respect to the possibility of its use as an electrode material for energy storage. To evaluate electrochemical characteristics of electrodes, the cyclic voltammetry (CV) and chronopotentiometric (CP) techniques were used. It is shown that phosphomolybdic acid immobilized on conductive C45 carbon black surface is stable in strong alkaline solution. The influence of the modification of C45 carbon black with H3PMo12O40 on the capacity of a composite electrode was studied and discussed.
W pracy przedstawiono badania nanokompozytu sadza węglowa C45-kwas fosforomolibdenowy-polifluorek winylidenu (C45-PMA- -PVDF) w 6M KOH pod kątem możliwości zastosowania go jako materiału elektrodowego do magazynowania energii. Do oceny właściwości elektrochemicznych badanych elektrod wykorzystano woltamperometrię cykliczną i galwanostatyczną technikę ładowania-rozładowania. Wykazano, że kwas fosfomolibdenowy unieruchomiony na powierzchni przewodzącej sadzy węglowej C45 jest stabilny w roztworze silnie alkalicznym. Przedstawiono i omówiono wpływ modyfikacji sadzy C45 za pomocą H3PMo12O40 na pojemność elektrody kompozytowej.
Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).