The effect of diffusion treatment of double (Al/Zr and Zr/Al) coatings on the microstructure of the system coating/Ni substrate

Double layers of aluminum (1 um thick) and zirconium (1 um thick) or zirconium (1 um thick) and aluminum (1 um thick) were deposited by the EB-PVD method. Adhesion evaluation of the layers was made using the scratch test. The layers were subjected to diffusion treatment at 1050°C for 2 h in the argon atmosphere. The linear and microarea chemical composition on the cross-section was made. Layers obtained by the EB-PVD method have good adhesion to the substrate. Diffusion treatment of Zr/Al layers leads to formation of Ni5Zr phases on the distance of 5 17 um from the surface, whereas the diffusion treatment of Al/Zr layers leads to the fonnation ofNi5Zr phases near the surface.

---

Powłoki Zr/Al o grubości (1+1) um oraz Al/Zr o grubości (1+1) um wytworzono na podłożu niklowym metodą EB-PVD. Przyczepność powłok do podłoża niklowego oceniano metodą zarysowywania (scratch-test). Wygrzewanie dyfuzyjne powłok prowadzono w temperaturze 1050°C przez 2 h. Analizę składu chemicznego na przekroju warstwy wykonano metodą mikroanalizy rentgenowskiej EDS. Uzyskane powłoki wykazały dobrą przyczepność do podłoża. Wygrzewanie powłok Zr/Al powodowało uzyskanie faz Ni5Zr w odległości ok. 5÷7 um od powierzchni, natomiast po wygrzewaniu powłok Al/Zr fazy Ni5Zr obserwowano w pobliżu powierzchni.