Crease-resistant Finish of Linen/Viscose Blend Fabrics

Linen/viscose blend fabrics are treated in different conditions with various concentrations of polycarboxylic acids (BTCA, CA, GA and MA) and N-methylol reagent (DMDHEU) with a relevant catalyst. The characterisation of such fibres is dependent on the degree of crosslinking, which is evaluated by the dry wrinkle recovery angle and tensile strength retention. In trials BTCA showed much better effects on the crease resistant finish of linen/viscose blend fabrics; when comparing the mixture of polycarboxylic acids, BTCA/GA treatment also gives moderate effects. High temperature curing is a handicap for linen/viscose blend fabric treatment when considering strength loss, whereas DMDHEU solutions give better results due to their lower acidity. In order to optimise the crease resistant finish of linen/viscose blend fabrics, it is acceptable to add a triethanolamine additive with the same ratio of the catalyst and cure at 160°C.

---

Tkaniny wykańczane były za pomocą kwasów polikarboksylowych (BTCA, CA, GA i MA) o różnym stężeniu oraz N-hydroksymetylowego reagentu (DMDHEU) z dodatkiem odpowiedniego katalizatora. Charakterystyka obrabianych włókien zależy od stopnia usieciowania, ocenianego poprzez kąt odprężności i zmianę wytrzymałości na rozciąganie. Najlepsze wyniki uzyskano przy stosowaniu BTCA, a umiarkowane przy stosowaniu BTCA/GA. Optymalna temperatura obróbki wykańczającej wynosiła 160°C natomiast przy 180°C utrata wytrzymałości mechanicznej po obróbce był mniejsza. Korzystne wyniki uzyskuje się przy zastosowaniu katalizatora w postaci trietanoloaminy.

---

W bibliografii brak pozycji 11.