Tribological properties of Ti/A-C:H nanocomposite carbon based coatings
The paper presents the results of mechanical and tribological tests of Ti/a-C:H nanocomposite carbon coatings and a-C:H hydrogenated carbon coating. All coatings were deposited by magnetron sputtering technique at various acetylene gas flows in a vacuum chamber, resulting in different coatings properties. The conducted study determines hardness, elasticity modulus, fracture resistance, and tribological properties – wear and friction coefficient of deposited coatings. The lowest wear and coefficient of friction were exhibited coatings deposited at higher acetylene flows, 15-20 sccm. However, they are atch testing is several times smaller than in a case of softer coatings deposited at lower acetylene flow up to 10 sccm.
W pracy przedstawiono wyniki badań mechanicznych i tribologicznych nanokompozytowych powłok węglowych Ti/a-C:H, które porównywano z właściwościami powłok węglowych a-C:H. Powłoki wytwarzano techniką magnetronowego rozpylania przy różnym przepływie acetylenu od 1 do 20 sccm przez komorę próżniową, co skutkowało różnymi właściwościami powłok. Przeprowadzone badania umożliwiły określenie twardości, modułu sprężystości, odporności na pękanie oraz właściwości tribologicznych – wskaźnika zużycia i współczynnika tarcia wytworzonych powłok. Najmniejszym zużyciem oraz najmniejszymi wartościami współczynnika tarcia charakteryzowały się powłoki wytworzone przy największych przepływach acetylenu 15–20 sccm. Natomiast są one kruche, a obciążenie krytyczne określone w teście zarysowania jest kilkukrotnie mniejsze niż dla miększych powłok osadzanych przy przepływie acetylenu do 10 sccm.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.