Phosphorus segregation in a Cr-Mo steel austenitised during various periods of time

In low-alloy steels and cast steels long-term operated in the equipment of conventional power industry phosphorus is the most harmful impurity, which segregates to grain boundaries and interphase boundaries causing a decline of strength properties, which at the operating conditions of high temperature and pressure makes a major problem. The paper presents results of studies on phosphorus segregation in a Cr-Mo steel after various periods of austenitising. The phosphorus segregation depth was assessed using the method of nickel plating of the studied steel surface. Results obtained for four austenitising periods allowed selecting the optimum parameters of heat treatment. Structural examinations were carried out using optical and scanning microscopy.

---

W niskostopowych stalach i staliwach eksploatowanych długotrwale w urządzeniach konwencjonalnej energetyki fosfor jest najbardziej szkodliwą domieszką, która segreguje do granic ziaren i granic międzyfazowych powodując spadek własności wytrzymałościowych, co przy warunkach pracy temperatura i ciśnienie stanowi poważny problem. W artykule przedstawiono wyniki badań segregacji fosforu w stali Cr-Mo po różnych czasach austenityzowania. Oceny głębokości segregacji fosforu dokonano metodą niklowania powierzchni badanej stali. Uzyskane wyniki dla czterech czasów austenityzowania pozwoliły wytypować najbardziej optymalne parametry obróbki cieplnej. Badania strukturalne przeprowadzono za pomocą mikroskopii optycznej i skaningowej.