Influence of galvanizing time on microstructure and microhardness of coating layers on selected structural steels

Changes in microstructure and microhardness are reported, depending on the processing parameters of galvanizing Fe-0.4Mn-0.02Si (S235) and Fe-1.4Mn-0.2Si (S355) steel substrates. The thickness of the coatings depended primarily on the dipping time, 4 and 8 min, which was confirmed by magnetic measurements. XRD analysis and SEM observations revealed typical structures of galvanized coatings, composed of η, ζ, δ and Γ. Microhardness measurements showed that the inner layer δ has the highest microhardness and the phase η has the lowest microhardness. Zn coatings on the Fe-0.4Mn-0.02Si substrate (very low Si content) are characterized by higher adhesion and durability compared to the coatings on Fe-1.4Mn- 0.2Si (higher silicon content).

---

Przedstawiono zmiany mikrostruktury i mikrotwardości w zależności od parametrów procesu cynkowania na podłożu stali Fe-0,4Mn-0,02Si (S235) i Fe-1,4Mn-0,2Si (S355). Grubość powstałych powłok zależała przede wszystkim od czasu zanurzenia (4 i 8 min), co potwierdziły pomiary magnetyczne. Analiza XRD i obserwacje SEM ujawniły typowe struktury powłok ocynkowanych, złożone z η, ζ, δ i Γ. Pomiary mikrotwardości wykazały, że warstwa wewnętrzna δ ma największą mikrotwardość, a warstwa η najmniejszą. Powłoki Zn na podłożu Fe-0,4Mn-0,02Si (bardzo mała zawartość Si) charakteryzują się lepszą przyczepnością i trwałością w porównaniu z powłokami na Fe-1,4Mn-0,2Si (większa zawartość Si).