Ni-Pt sintered electrode for hydrogen evolution from alkaline solutions

An influence of platinum grains deposit on the surface of nickel powder sintered electrode on electrochemical processes of hydrogen generation is presented and discussed in this paper. The sinters of metallic nickel were obtained as a support for platinum grains by oxidation/reduction (air/H2) process. Platinum grains were added onto the surface of Ni supports and then sintered during the successive oxidation/reduction. The morphology characteristic of sinters was carried out with the application of SEM/EDS methods. The electrochemical properties of Ni and Ni-Pt electrodes were examined by potentiostatic method. It was found that platinum grains deposited on the surface of Ni sinters were well-adherent and stable. The presence of platinum grains on nickel sintered electrodes results in a slight increase of the measured current density of hydrogen evolution reaction.

---

W artykule przedstawione są wyniki badań nad otrzymywaniem porowatych elektrod niklowych z depozytem ziaren platyny na powierzchni spieku Ni. Spieki Ni oraz Ni-Pt otrzymano w sekwencyjnym procesie utleniania (powietrze) i redukcji (wodór). Charakterystykę morfologii i składu chemicznego otrzymanych spieków przeprowadzono metodą SEM/EDS. Wpływ depozytu platyny na proces wydzielania wodoru ze środowiska alkalicznego zbadano metodą potencjostatycznej polaryzacji elektrochemicznej. Stwierdzono, że depozyt ziarna Pt dobrze przylega do powierzchni spieków Ni oraz jest stabilny w trakcie ich pracy w roztworze KOH. Obecność depozytu Pt na powierzchni spieków Ni skutkuje nieznacznym wzrostem gęstości prądu związanego z reakcją wydzielania wodoru z roztworu.