Alkaline leaching of amphoteric elements from powdered, overstoichiometric hydride material

The alkaline preferential dissolution of amphoteric elements from overstoichiometric, powdered hydrogen absorbing material of LaNi4.5Co0.5(AlZnSn)0.35 composition has been studied using ICP AES method. The observations of structure changes of the as received and leached material particles have been studied by XRD and TEM techniques. It has been shown that during 50 h exposure of the powder in 6 M KOH (38oC) over 50% of amphoteric elements are selectively etched from the tested material. At the same time, as a result of etching, the surface layers of powder particles undergo strong development.

---

Metodą ICP AES analizowano preferencyjne wytrawianie pierwiastków amfoterycznych z nadstechiometrycznego materiału wodorochłonnego o składzie LaNi4.5Co0.5(AlZnSn)0.35. Zmiany strukturalne wyjściowych i trawionych cząstek materiału obserwowano za pomocą technik XRD i TEM. Pokazano, że 50-godzinna ekspozycja badanego proszku w 6 M KOH (38oC) prowadzi do selektywnego roztworzenia ponad 50% pierwiastków amfoterycznych obecnych w wyjściowym materiale. Jednocześnie, w wyniku wytrawiania proszku, powierzchnia zewnętrznych warstw cząstek ulega silnemu rozwinięciu.