Microstructure of joints made of duplex steel LDX 2101 using concentrated beams and various welding rates
The article presents tests concerned with the welding of duplex steel LDX 2101 using a laser beam, an electron beam and various welding rates. Flat butt joints were made using the laser beam and welding rates of 1 m/min and 2 m/min as well as the electron beam and welding rates of 0.2 m/min and 2 m/min. Microscopic metallographic examinations involved the use of light microscopy. The microstructure of individual areas of the test joints was revealed using colour electrolytic etching. Structural components in individual areas of the joints were identified using NIS Elements-AR software tools (Nikon). The same software was used for measuring the width of the joints and the height of excess weld metal. Test results were used to formulate related conclusions.
W artykule przedstawiono próby spawania stali duplex LDX 2101 wiązką laserową oraz wiązką elektronów z różnymi prędkościami. Wykonano złącza doczołowe płaskie z następującymi prędkościami spawania: wiązką laserową 1 m/min i 2 m/min, wiązką elektronów 0,2 m/min oraz 2 m/min. Przeprowadzono badania metalograficzne mikroskopowe z użyciem mikroskopii świetlnej. Mikrostrukturę poszczególnych obszarów badanych złączy ujawniono przy zastosowaniu barwnego trawienia elektrolitycznego. W poszczególnych obszarach złączy zidentyfikowano składniki strukturalne oraz dokonano pomiarów szerokości spoin w złączach i wysokości nadlewów lica spoin za pomocą narzędzi programu NIS Elements-AR firmy Nikon. Z przeprowadzonych badań sformułowano wnioski.
Opracowanie rekordu ze środków MNiSW, umowa nr POPUL/SP/0154/2024/02 w ramach programu "Społeczna odpowiedzialność nauki II" - moduł: Popularyzacja nauki (2025).