Mechanical properties of P91 and PB2 steel after long-term ageing at 620°C
The article presents the results of research on mechanical properties of martensitic steels, X10CrMoVNb9-1 (P91) and X13CrMoCoVNbNB9-2-1 (PB2), as-received and after 50,000 hours of ageing at 620˚C. The scope of the tests of mechanical properties included a Vickers hardness test, Charpy impact test, and static tensile test. As received, the investigated steels were characterised by relatively high mechanical properties. The long-term effect of temperature and time contributed to a relatively slight decrease in the strength properties and hardness of the tested steels. However, a considerable decrease in the ductility of these alloys was observed. The decrease in mechanical properties after long-term ageing was smaller in the case of the PB2 steel, which was attributed to the beneficial effect of microalloying boron.
W artykule przedstawiono wyniki badań właściwości mechanicznych stali martenzytycznych X10CrMoVNb9-1 (P91) i X13CrMoCoVNbNB9-2-1 (PB2) w stanie dostawy oraz po 50 000 godzinach starzenia w temperaturze 620˚C. Zakres badań właściwości mechanicznych obejmował pomiar twardości metodą Vickersa, próbę udarności oraz statyczną próbę rozciągania. W stanie dostawy badane stale charakteryzowały się względnie wysokimi właściwościami mechanicznymi. Długotrwałe oddziaływanie temperatury i czasu przyczyniło się do względnie niewielkiego spadku właściwości wytrzymałościowych i twardości badanych stali. Obserwowano natomiast znaczące obniżenie ciągliwości tych stopów. Spadek właściwości mechanicznych po długotrwałym starzeniu był mniejszy w przypadku stali PB2, co przypisano korzystnemu działaniu mikrododatku boru.
Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).