In this paper, based on a quantitative analysis of the parameters of plasma hardfacing of C45 steel with CastoMag 45554S wire, an optimisation of the hardfacing process parameters has been carried out. Experimental researches were carried out on the basis of an orthogonal plan, and the optimum hardfacing parameters, e.g.: intensity, voltage, wire feeding speed, were determined by the multiple regression method and the Taguchi method. It was found that the main current of the plasma arc had the greatest influence on the value of the fusion index. The highest S/N value was obtained for the following parameters: I = 120 A, U = 31 V, vn = 0.75 m/min, vd = 3.9 m/min, z = 12 mm.

---

W oparciu o ilościową analizę parametrów napawania plazmowego stali C45 drutem CastoMag 45554S dokonano optymalizacji parametrów procesu napawania. Badania realizowano na podstawie planu ortogonalnego, a optymalne parametry napawania np.: natężenie, napięcie, prędkość podawania drutu zostały wyznaczone metodą regresji wielokrotnej oraz metodą Taguchi. Ustalono, że największy wpływ na wartość współczynnika wtopienia ma natężenie prądu głównego łuku plazmowego. Największą wartość współczynnika S/N uzyskano przy parametrach: I = 120 A, U = 31 V, vn = 0,75 m/min, vd = 3,9 m/min, z = 12 mm.