The Properties and Microstructure of AlTi6/Al2O3 Joints

The influence of the titanium addition into aluminium on the bond strength properties and structure of interface of the AlTi6/Al2O3 joints was investigated. The bond strength of the metal/Al2O3 joints was determined by the push-off test. Addition of 5.9 wt.%. Ti to Al caused the reduction of shear strength of the AlTi6/Al2O3 joints. The investigations by mean of electron microscopy equipped with a spectrometric system for microanalysis of the chemical composition revealed TiAl3 phases formed at the AlTi6/Al2O3 interface. Oxygen was detected in some areas of TiAl3 phases. Finally, this structure of the AlTi6/Al2O3 interface was responsible for lower bond strength comparing to properties of the Al/Al2O3 joints.

---

W pracy przedstawiono badania dotyczące wpływu dodatku tytanu do aluminium na wytrzymałość na ścinanie oraz mikrostrukturę połączenia AlTi6/Al2O3. Wyniki wykazały, że dodanie tytanu do aluminium wpływa na obniżenie wytrzymałość na ścinanie badanego połączenia. Badania mikrostrukturalne (SEM oraz TEM) połączone z analizą składu chemicznego wykazały powstanie wydzieleń fazy TiAl3 na granicy rozdziału połączenia. W obszarach fazy TiAl3 obserwowano obecność tlenu. Tworzenie nowych faz na granicy rozdziału połączenie AlTi6/Al2O3 odpowiada za obniżenie wytrzymałości w porównaniu z połączeniem Al/Al2O3.