Waxs Studies of Salix Viminalis Wood Susceptibility to Alkali Treatment

Comminuted willow wood (Salix viminalis) was treated with sodium hydroxide solutions of 10, 15, 20 and 25% NaOH concentration, for 15, 30, 45, 60 and 90 minutes for each case of NaOH concentration. The WAXS method was used to estimate the content of cellulose II with reference to a global amount of crystalline cellulose included in the wood and gravimetric measurements were performed to estimate the mass losses caused by the alkali treatment of the wood. As a result, the changes in both the index of cellulose II content and the WPG index for the treatment period and for the NaOH concentration have been determined. In particular, it was established that: i) no cellulose I/cellulose II polymorphic transformation occurs even with 90-minute action of 10% NaOH solution, ii) the index of cellulose II content ranges from 46% with 15-minute action of 15% NaOH solution to 66% with 90-minute action of 25% NaOH solution, iii) irrespective of NaOH concentration, the WPG index approaches ca. -20% with the 15-minute treatment and then increases only to ca. -24% with the 90-minute treatment.

---

Na rozdrobnione drewno wierzbowe (Salix viminalis) działano roztworami NaOH o stężeniach: 10%, 15%, 20% i 25% przez 15, 30, 45, 60 i 90 minut dla każdego ze stężeń. Metodą WAXS wyznaczono zawartość celulozy II (wskaźnik δII ) w drewnie, a techniką grawimetryczną określono ubytki masy próbek drewna poddanego działaniu NaOH (wskaźnik WPG). Stwierdzono, że działanie 10% NaOH przez 90 minut nie powoduje przemiany polimorficznej celulozy I do celulozy II. Zawartość celulozy II wynosiła 46% dla próbek poddanych działaniu 15% roztworem NaOH przez 15 minut i 66% w wyniku działania 25% NaOH przez 90 minut. Natomiast wskaźnik WPG wynosił -20% po 15 minutowym działaniu alkaliów oraz -24% po 90 minutach ich działania.