Plasma Welding of Steel CPW 800
The article is concerned with issues related to the plasma welding of steel CPW 800 using titanium and niobium microagents. Plasma welding tests involving sheets subjected to TMCP were performed with various linear energy values. Welded joints were subjected to macro and microscopic metallographic tests, hardness measurements (involving the base material, HAZ and weld) as well as tensile and bend tests. The strength of the welded joints obtained in the tests was greater than that of the base material; a slight increase in the hardness of joint area ensured its relatively high plasticity.
Praca dotyczy problematyki spawania plazmowego stali typu CPW 800 z mikrododatkami Ti i Nb. Próby spawania plazmowego blach walcowanych termomechanicznie prowadzono z różnymi energiami liniowymi. Dla wykonanych połączeń spawanych przeprowadzono badania metalograficzne makroskopowe i mikroskopowe oraz określono twardość materiału rodzimego, strefy wpływu ciepła i spoiny. Przeprowadzono badania wytrzymałości na rozciąganie oraz próbę zginania. Wytrzymałość uzyskanych połączeń spawanych była większa od wytrzymałości materiału podstawowego a nieznaczny wzrost twardości obszaru złącza zapewnia relatywnie dużą jego plastyczność.
Wersja polska artykułu w wydaniu papierowym s. 28-32.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.