Structural transformation of terpolymer poly(L-lactide-glycolide-trimethylene carbonate) with shape memory effect during the degradation process

The purpose of this study was to analyze the changes of the structure of shape memory polymer (SMP) surgical staple made from poly(L-lactide-glycolide-trimethylene carbonate) during in vitro degradation. It is crucial to understand the structure and properties of SMP biomedical polymers during the degradation process as their biodegradation rate should match the therapeutic period. It was confirmed that degradation results in a decrease of Tg and that degradation at a temperature above Tg involves faster dynamics. The hydrolysis of amorphous regions lead to increased crystallinity and erosion of the polymer.

---

Analizowano zmiany zachodzące w strukturze klamry chirurgicznej wykonanej z polimeru z pamięcią kształtu, podczas degradacji prowadzonej w warunkach in vitro. Istotne znaczenie ma określenie wpływu tych zmian na właściwości fizyczne materiału klamry, ponieważ biodegradacja nie może zakłócać procesu terapeutycznego. Stwierdzono, że degradacja polimeru prowadzi do obniżenia wartości temperatury zeszklenia (Tg). W temperaturze powyżej wartości Tg obserwowano zwiększoną dynamikę procesu degradacji. W wyniku hydrolizy obszarów amorficznych zwiększał się stopień krystaliczności, a w skali mikroskopowej następowała erozja tworzywa.