Solidification of Fe-Zn sublayers during galvanizing process

The study describes the mechanism of structure formation in protective coating, growing on iron surface during hot-dip galvanizing. As a first stage of the galvanizing process, immediately after the iron sample has been dipped in galvanizing bath, a layer of frozen zinc is crystallizing on the sample surface. Next, as a result of isothermal solidification, an alloyed layer of the coating; composed of the sublayers of intermetallic Fe-Zn phases, is formed. At the initial stage of the existence of the alloyed layer, another layer, that of undercooled liquid, is formed on the surface of iron dipped in liquid zinc. As a result of peritectic reactions under metastable conditions, the individual phases are born, forming sublayers in the expected sequence of Γ1, δ and ζ.

---

W pracy opisano mechanizm kształtowania się struktury powłoki ochronnej podczas cynkowania zanurzeniowego. Podczas pierwszego etapu procesu, zaraz po zanurzeniu wyrobu w ciekłym cynku, w pierwszej tworzy się na jego powierzchni kolejności warstwa namrożonego cynku. Warstwa ta roztapia się po pewnym czasie. Następnie w wyniku krystalizacji izotermicznej tworzy się warstwa stopowa powłoki, składająca się z cząstkowych warstw faz międzymetalicznych Fe-Zn. W początkowym okresie krystalizacji warstwy stopowej na powierzchni wyrobu wprowadzonego do ciekłego cynku powstaje warstwa przechłodzonej cieczy. W wyniku reakcji perytektycznych w warunkach metastabilnych kształtują się poszczególne fazy, tworząc podwarstwy faz w oczekiwanej kolejności: Γ1, δ oraz ζ.