Investigation of solidification process and microstructure examination of AlCu4Ni2Mg2 aluminium alloy

The main objective of this work was to examine a solidification process of AlCu4Ni2Mg2 alloy and analyze morphology and composition of the complex microstructure of intermetallic phases in as-cast condition. To study the solidification process differential scanning calorimetry (DSC) was used. To identify intermetallics in AlCu4Ni2Mg2 alloy optical light microscopy (LM), X-ray diffraction (XRD), scanning (SEM) and transmission (TEM) electron microscope and were used. The results show that the as-cast microstructure of AlCu4Ni2Mg2 alloy after slow solidification at a cooling rate 5°/min, consisted: dendrites of α-Al and intermetallic phases Al₇Cu₄Ni, Al₆Fe, S-Al₂CuMg, and Al₃(CuFeNi)₂ and Al₂Cu.

Prowadzono analizę procesu krystalizacji oraz składu chemicznego i morfologii składników fazowych mikrostruktury stopu AlCu4Ni2Mg2 w stanie lanym. W analizie procesu krystalizacji stopu stosowano metodę różnicowej kalorymetrii skaningowej (DSC). Identyfikację składników fazowych mikrostruktury stopu AlCu4Ni2Mg2 prowadzono metodami mikroskopii świetlnej (LM), elektronowej: skaningowej (SEM) i transmisyjnej (TEM) oraz dyfrakcji rentgenowskiej (XRD). Analiza uzyskanych wyników badań pozwoliła ustalić, że mikrostruktura stopu AlCu4Ni2Mg2, kształtowana w procesie krystalizacji z małą prędkością chłodzenia 5°C/min, składa się z dendrytów roztworu stałego α-Al oraz wydzieleń faz międzymetalicznych: Al₇Cu₄Ni, Al₆Fe, S-Al₂CuMg, Al₃(CuFeNi)₂ i Al₂Cu.