Tribological Properties of Medium-Carbon Steel after Nitriding Combined with Subsequent Oxidation and Impregnation

The paper presents the results of examinations of tribological and corrosion properties of the layers produced on a C45 medium-carbon steel surface in the gas nitriding process combined with subsequent treatment – oxidation and impregnation of corrosion inhibitor. Investigations of the microstructure of these layers and their phase composition were carried out. Hardness of the layers was measured by Vickers method. Tribological properties (linear wear) of the layers were performed by means of the three-cylinder-cone method. Resistance to corrosion was determined by electrochemical methods. The investigations showed that the linear wear of the C45 steel samples with the layers produced in the combined processes of nitriding with subsequent oxidation and impregnation was smaller than that of steel samples without layers. Moreover, the corrosion resistance of these layers in aggressive solutions containing chloride ions was very good.

W pracy omówiono wyniki badań właściwości tribologicznych i korozyjnych warstw wytwarzanych na powierzchni stali średniowęglowej C45 w procesie azotowania gazowego połączonym z następną obróbką – utlenianiem i impregnacją inhibitorem korozji. Przeprowadzono badania mikrostruktury tych warstw, jak również ich składu fazowego. Twardość warstw była mierzona metodą Vickersa. Właściwości tribologiczne (zużycie liniowe) warstw oceniano metodą trzy wałeczki–stożek. Badania odporności na korozję przeprowadzono metodami elektrochemicznymi. Badania wykazały, że zużycie liniowe próbek ze stali C45 z warstwami wytworzonymi w połączonych procesach azotowania z następnym utlenianiem i impregnacją, było mniejsze niż próbek ze stali bez warstw. Ponadto odporność korozyjna tych warstw w agresywnych roztworach zawierających jony chlorkowe była bardzo dobra.