Influence of the filler on the density profile of wood polymer composites. WPC panels with HDPE matrix composites made in two stages were tested: 1 - obtaining WPC granulate using the extrusion method, 2 - production of panels by flat pressing in the form. As a filler, sawdust was used with two degrees of fineness (about 10 - 35 mesh and below 35 mesh) and three levels of content (40, 50 and 60%). In total, 6 panel variants were created for which the density and density profile in the cross-section were determined. It was found that panels with a filler content of 40% are characterized by a uniform flat density profile. The increase in filler content (up to 50 - 60%) affects the density reduction in the core zone of the panel. The density and density profile of panels from WPC composites does not depend on the size of the filler particles.

Wpływ napełniacza na profil gęstości kompozytów drzewno polimerowych. Przeprowadzono badania płyt z kompozytów WPC o matrycy HDPE wytworzonych dwuetapowo: 1 – pozyskanie granulatu WPC metodą extruzji, 2 – wytworzenie płyt metodą prasowania płaskiego w formie. Jako napełniacz zastosowano trociny o dwóch stopniach rozdrobnienia (ok. 10 – 35 mesh i poniżej 35 mesh) i 3 poziomach zawartości (40, 50 i 60%). Łącznie wytworzono 6 wariantów płyt dla których określono gęstość i profil gęstości na przekroju poprzecznym. Ustalono, że płyt o zawartości napełniacza na poziomie 40% charakteryzują się jednolitym płaskim profilem gęstości. Wzrost zawartości napełniacza (do 50 – 60%) wpływa na obniżenie gęstości w strefie środkowej płyty. Gęstość i profil gęstości płyt z kompozytów WPC nie zależy od wielkości cząstek napełniacza.