Effect of Gamma Radiation on the Mechanical Properties of Natural Fabric Reinforced Polyester Composites

Two types of composites: (1) pineapple fabric reinforced polyester resin (pineapple/PR) and (2) jute fabric reinforced polyester resin (jute/PR) were prepared and the mechanical properties investigated for various gamma radiation doses ranging from 100-500 krad. Properties like tensile strength, Young’s modulus, elongation-at-break, bending strength, bending modulus and impact strength were increased significantly by 19%, 32%, 45%, 32%, 47% and 20%, respectively, at a dose of 300 krad for pineapple/PR, and by 47%, 49%, 42%, 45%, 52% and 65%, respectively, at a dose of 200 krad for the jute/PR composite in comparison to the non-irradiated composite. Gamma radiation improved the mechanical properties, but overdoses of radiation even caused a reduction in them.

W pracy przygotowano dwa rodzaje kompozytów (1) żywica poliestrowa wzmocniona tkaniną ananasową (Pineapple/PR) i (2) żywica poliestrowa wzmocniona tkaniną jutową (Jute/PR), a następnie zbadano wpływ na właściwości mechaniczne kompozytów różnych dawek promieniowania gamma w zakresie od 100-500 krad. Właściwości takie jak wytrzymałość na rozciąganie, moduł Younga, wydłużenie przy zerwaniu, wytrzymałość na zginanie, moduł zginania i wytrzymałość na uderzenia zostały znacznie polepszone odpowiednio o 19%, 32%, 45%, 32%, 47% i 20% w dawce 300 krad dla Pineapple/PR, podczas gdy odpowiednio 47%, 49%, 42%, 45%, 52% i 65% w dawce 200 krad dla kompozytu Jute/PR w porównaniu z kompozytem nienapromieniowanym. Stwierdzono, że promieniowanie gamma poprawia właściwości mechaniczne kompozytów, ale przy zastosowaniu nadmiernych dawek promieniowania właściwości te ulegają pogorszeniu.