Properties of carbide layers produced by means of the vacuum titanizing process combined with galvanic treatment

A new technological processes combining a vacuum titanizing with a preliminary electrolytic deposition of Co-W or Ni-Mo alloys on the tool steel surface have been proposed to increase the corrosion resistance of the carbide layers of the TiC type. As a result, composite carbide layers of the TiC+(Co-W) and TiC+(Ni-Mo) type on the steel surfaces have been obtained. It has been proved that the wear resistance by friction of these composite layers produced by means vacuum titanizing of steel covered with electrolytic coatings is as good as the TiC carbides layers produced on the steel surface without electrolytic coatings, but their corrosion resistance is higher.

W pracy przedstawiono wyniki badań dotyczących właściwości użytkowych warstw kompozytowych typu TiC+(Co-W) oraz TiC+(Ni-Mo) wytwarzanych w procesie tytanowania próżniowego na powierzchni stali X210Cr12 pokrytej elektrolitycznie stopami Co-W lub Ni-Mo. Określono właściwości tribologiczne oraz odporność korozyjną warstw. Stwierdzono, że odporność na zużycie przez tarcie warstw kompozytowych typu TiC+Co-W) oraz TiC+(Ni-Mo) wytwarzanych w procesie chromowania próżniowego na stali pokrytej powłokami Co-W lub Ni-Mo, jest równie dobra, jak warstw węglikowych typu TiC, wytwarzanych bez wstępnego osadzania powłoki elektrolitycznej, natomiast ich odporność korozyjna jest kilkakrotnie większa.