Crystalline engineering of coordinate polymers based on multi-core building blocks

In order to obtain new multi-core connections with the participation of high-spin clusters, three clusters, used as the basic building blocks and a range of organic ligands as linkers, have been selected . In addition, two lanthanide ions Ln3 + with such characteristics as high spin (gadolinium) and strong magnetic anisotropy (dysprosium) have been selected. It was assumed that this strategy of synthesis would achieve new materials exhibiting SMM behavior and a strong low-temperature magnetocaloric effect. As part of the thesis, the number of syntheses was caried out in order to obtain new coordination networks. This gave us four new systems, in which the content of C, N, H (elemental analysis) and metal (X-ray microanalysis SEM) were analyzed. Also the IR spectrum of each of the received systems were examined. In other cases, the synthesis could not receive systems suitable for further testing.

W celu otrzymania nowych połączeń wielordzeniowych z udziałem klastrów wysokospinowych wybrano trzy klastry pełniące funkcję podstawowych bloków budulcowych oraz szereg ligandów organicznych jako łączników. Dodatkowo wybrano dwa jony lantanowców Ln3+ posiadające takie cechy jak duży spin (gadolin) oraz silną anizotropię magnetyczną (dysproz). Założono, że taka strategia syntezy pozwoli na uzyskanie nowych materiałów wykazujących zachowania typu SMM oraz silnego niskotemperaturowego efektu magnetokalorycznego. W ramach pracy licencjackiej przeprowadzono szereg syntez mających na celu otrzymanie nowych sieci koordynacyjnych. W wyniku tego otrzymano cztery nowe układy, które poddano analizie zawartości C, N, H (analiza elementarna) oraz metali (mikroanaliza rentgenograficzna SEM). Zbadano również widma w podczerwieni IR każdego z otrzymanych układów. W przypadkach pozostałych syntez nie udało się otrzymać układów odpowiednich do dalszych badań.