This study was attempted to demonstrate that modifications of zeolites such as dealumination and desilication led to the generation of an additional mesopore system within the zeolite grains. The studies were focused on 8 MR and 12 MR zeolies. The main part of work is devoted to detailed characterization of structural/textural and acidic properties of zeolites FER of different Si/Al ratios (23 and 9). The textural parameters were examined with low-temperature nitrogen sorption studies. For acidity characterization the IR spectroscopy was employed with pyridine as probe molecule. It has been demonstrated that the sequential acid/base treatment is a suitable method for zeolite hierarchization.

W pracy wykazano, że modyfikacje zeolitów takie jak dealuminacja oraz desilikacja pozwalają na wygenerowanie dodatkowego systemu mezoporów w obrębie ziaren zeolitów. Modyfikacji poddano zeolit typu FER o Si/Al=9 oraz 23. W pracy przedstawiono procedury modyfikacji badanych preparatów. Dzięki zastosowaniu różnych stężeń czynnika desilikującego jakim był LiOH oraz czynnika dealuminującego w postaci HNO3, uzyskano szereg preparatów, które charakteryzują się różnym stopniem hierarchiczności. W oparciu o badania XRD wykazano, że traktowanie zeolitów kwasami i alkaliami o różnych stężeniach nie wpływa negatywnie na krystaliczność badanych materiałów. W pracy przedstawiono wyniki badań z wykorzystaniem niskotemperaturowej sorpcji azotu dotyczące parametrów teksturalnych otrzymanych materiałów. Dodatkowo, przeprowadzono również pomiary ilościowe IR stężeń centrów kwasowych Brønstea i Lewisa. W tym celu zastosowano standardową metodę badań IR z wykorzystaniem pirydyny jako cząsteczki sondy.