Optymalizacja fotoredukcji H2O2 w obecności TiO2 o strukturze anatazu

The main aim of this study was to analyze the impact of the crystallographic planes exposure on the photoreduction of hydrogen peroxide. Anatase titanium dioxide was synthesized with increased exposure of selected planes. In this hydrothermal process sodium fluoride was used as a capping agent. The obtained materials were named according to their anatase (A) crystal phase, and the most abundant facet. Band gap of the synthesized materials was obtained using DRS. SEM images of the materials were also taken. The last step involved photocatalytic activity tests in various conditions. These tests provided information on overall OH radical generation in presence and lack of H2O2 in the system. Influence of hole scavenger (EDTA) was also investigated.

Celem pracy była analiza wpływu ekspozycji płaszczyzn krystalograficznych na fotoredukcję nadtlenku wodoru. Zsyntetyzowano tlenek tytanu(IV) o strukturze anatazu o zwiększonej ekspozycji wybranych płaszczyzn. W tym celu wykorzystano metodę hydrotermalną z użyciem fluorku sodu. Zsyntetyzowano materiały A101, A001 oraz A100 i dodatkowo AK-1, A001c, gdzie: A oznacza anataz, trzy cyfry definiują wskaźniki Millera dominujących płaszczyzn. Przy pomocy pomiarów UV-Vis wyznaczono przerwy wzbronione poszczególnych materiałów. Wykonano analizę materiałów za pomocą skaningowej mikroskopii elektronowej. Ostatnim etapem było wykonanie testów fotokatalitycznych w różnych układach. Testy te pozwoliły uzyskać informacje o właściwościach fotokatalitycznych zsyntetyzowanych materiałów. Badano również wpływ dodatku wygaszacza dziur (EDTA) na proces fotoredukcji H2O2.